OVERVIEW
|
|
FC-SEAL (ZSWP100) is a water proofing membrane developed by Fullchance Rubber. The rubber membrane has 100 % EPDM polymer content making it an ideal choice for the water-proofing of roofs, swimming pools, foundations for civil constructions, soak pits for animal feed, gobar gas plants, canals, etc. With a life that spans 20 years FC-SEAL (ZSW100) is the best choice for waterproofing applications.
FC-SEAL (ZSWP100) is produced in accordance to ASTM D4637 and ASTM 6134. The sheet conforms to all requirements for non-reinforced black EPDM rubber sheet for use in waterproofing applications.
FC-SEAL (ZSWP100) is available in the following dimensions:
|
- Thickness: 1mm to 1.5 mm
-
Length: 10 mtrs to 30 mtrs rolls
- Width: 1 mtrs to 1.5 mtrs
- Packing: Rolls are wound on 3 inch paper core with outer surface of rolls covered with HDPE
FC-SEAL (ZSWP100) single ply black membranes are light weight and have exceptional long lasting elasticity permitting the materials to withstand Building movement, Expansion - Contraction of Building surfaces, High resistance to Ozone and weather as they are known as “Crack-less Rubbers”, Low Specific gravity - lightest among all rubbers, Widest Temperature range from - 50°C to + 150°C, Excellent Steam and Water Resistance.
|
| |
TECHNICAL SPECIFICATION - EPDM MEMBRANE BASED ON ASTM - D4637
|
| EPDM MEMBRANE BASED ON ASTM - D4637 |
|
PROPERTIES
|
TEST METHOD |
SPECIFICATION |
| Tolerance on Nominal Thickness,% |
ASTM D 412 |
15/-10 |
| Color |
Visual |
Black |
| HARDNESS |
ASTM D2240 |
65±10 Sh A |
| TENSILE STRENGTH ( min ) |
ASTM D412 |
90KGS. CM2 |
| ELONGATION AT BREAK ( min ) |
ASTM D412 |
350% |
| TEAR RESISTANCE kg/cm |
ASTM D624 method C |
30 |
| Drop in physical properties - Ageing |
|
|
| After 100°C for 600 Hrs |
|
|
| Tensile Strength min. |
ASTM D - 412 |
10% |
| Elongation ( % ) |
ASTM D - 412 |
30% |
| Tear resistance (kg/cm) |
ASTM - 412 |
15% |
| Linear dimensional change max. % |
ASTM D - 1204 |
+/- 2% |
| Ozone Resistance: On exposure to 100 ppm and Ozone in air 96 hrs.@ 40 C at 20 % strain |
ASTM D 1149 |
No crack |
| Glass transition Temperature : |
ASTM D - 746 |
-55 |
| Resistance Water absorption, after 7 days immersion in 70° C, % change in mass |
ASTM D 471 |
4.0 |
| Compression set, 22 Hrs. at 70°C |
ASTM D 395 |
24% |
| Specification No: ZRWP100/1 |
Rev. No.: 00 |
Rev. Date: 00 |
|
TECHNICAL SPECIFICATION - EPDM MEMBRANE BASED ON ASTM 6134
|
| EPDM MEMBRANE BASED ON ASTM 6134 |
|
PROPERTIES
|
TEST METHOD |
SPECIFICATION |
| Tolerance on Nominal Thickness,% |
ASTM D 412 |
15/-10 |
| Color |
Visual |
Black |
| HARDNESS |
ASTM D2240 |
65 ± 10 A |
| TENSILE STRENGTH ( min ) |
ASTM D412 |
90KGS.CM2 |
| ELONGATION AT BREAK ( min ) |
ASTM D412 |
300% |
| ABRASION RESISTANCE ( max ) |
ASTM D5963 |
250 mm3 |
| COMPRESSION SET (70° C/24 hrs) (max) |
ASTM D395 Method B |
24% |
| TEAR RESISTANCE (Angular) min |
ASTM D624 method C |
30 |
| Resistance to Heat Aging |
|
|
| Properties after 166 hrs @ 115°C |
ASTM D - 573 |
|
| Tensile Strength min. |
ASTM D - 412 |
85kgs. /Cm2 |
| Elongation ( % ) |
ASTM D - 412 |
210 |
| Linear dimensional change max. % |
ASTM D - 1204 |
+/-1 |
| Brittleness temperature °C |
ASTM D 746 |
-45 |
| Resistance water absorption, after 166Hrs. Immersion @ 70° C |
|
|
| % change in mass |
ASTM D 471 |
4.0 |
| Water Vapor Permeability Max. per-mills |
ASTM E 96 |
3.5 |
| Specification No: RSWP100/2 |
Rev. No: 00 |
Rev. Date: 00 |
|
| |
FC-SEAL TEST REPORT
|
| FC-SEAL TEST REPORT |
|
PROPERTIES
|
TEST METHOD
|
SPECIFICATION |
OBSERVATION |
| Color |
Visual |
Black |
Black |
| HARDNESS |
ASTM D2240 |
65 ± 10 A |
64,65,67 |
| TENSILE STRENGTH ( min ) |
ASTM D412 |
90KGS. CM2 |
100,105,98 |
|
ELONGATION AT BREAK
( min )
|
ASTM D412 |
300% |
400,450,400 |
|
ABRASION RESISTANCE
( max )
|
ASTM D5963 |
250 mm3 |
200 |
|
COMPRESSION SET
( 70° C / 24 hrs ) (max)
|
ASTM D395 METHOD B |
24% |
20 |
|
TEAR RESISTANCE (Angular) min
|
ASTM D624 method C |
30 |
34,35,31 |
| Resistance to Heat Aging |
|
|
|
|
Properties after 166 hrs @ 115°C
|
ASTM D - 573 |
|
|
| Tensile strength min. |
ASTM D - 412 |
85kgs. /Cm2 |
90,96,95 |
| Elongation (%) |
ASTM D - 412 |
210 |
350,350,375 |
|
Linear dimensional change max. %
|
ASTM D - 1204 |
+/-1 |
0.44 |
| Brittleness temperature° C |
ASTM D 746 |
-45 |
- |
|
Resistance water absorption, after 166Hrs. Immersion @ 70°C
|
|
|
|
| % change in mass |
ASTM D 471 |
4.0 |
3.45 |
|
Water Vapor Permeability Max. per-mils
|
ASTM E 96 |
3.5 |
- |
| Test report No: - ZSWP100/1 |
Rev. No: 00 |
|
Rev. Date: 00 |
|
| |
|