STORAGE TANK FABRIC
|
Feature
|
 |
-
High Temperature, solvent & oil resistance.
-
Applicable in solvent storage tank.
-
Fabric can be used by Aviation, Aerospace, Aircraft Division for Manufacturing defense products.
-
Available in different colors, sizes and thicknesses.
|
| |
|
|
|
| |
| Code: FC-FKM |
|
Insertion Fabric
|
Heat set Nylon 66 fabric
|
|
Polymer
|
Viton (FKM) / Viton (FKM)
|
|
Color
|
Black/ Black
|
|
Breaking Strength
|
Warp-260 kgs, Weft-250kgs, Warp- 572 lbs, Weft- 550 lbs
|
|
Min. Thickness
|
1.5 mm ± 0.05 mm, 0.059 inch ± 0.002”
|
|
Width Available
|
1.0 Mtr (39.37”) to 1.5 Mtr (60”)
|
|
Coated Fabric Weight
|
2600 gsm (± 5%), 76.44 oz/yd2 (±5%)
|
|
| |
 |
FURNASE CURTAINS / WELDING BLANKETS FABRIC
|
Feature
|
|
-
Available in different colors, sizes and thicknesses.
-
Basic product for High temperature Fabric expansion joints (Rubber Bellows).
-
It is used in furnace curtain, wielding blankets and defense application.
|
|
 |
|
| |
| Code: FC-SI |
|
Insertion Fabric
|
Fiber glass
|
|
Polymer
|
Silicon/ Silicon
|
|
Color
|
Brick Red / White
|
|
Breaking Strength
|
Warp- 170 kgs, Weft- 140 kgs, Warp- 374 lbs, Weft- 308 lbs
|
|
Min. Thickness
|
0.6 mm ± 0.05 mm, 0.023 inch ± 0.002”
|
|
Width Available
|
1.0 Mtr (39.37”) to 1.5 Mtr (60”)
|
|
Coated Fabric Weight
|
650 gsm (± 5%), 19.11 oz/yd2 (± 5%)
|
|
| |
 |
ANTI WICKING FABRIC
|
Feature
|
|
-
This has anti capillary quality which is used for Diaphragm Valve’s Application.
-
It can be easily used at 125˚c temperature.
-
It is good Oil & solvent resistance.
-
It is used for brake valves as insertion fabric.
|
| |
|
|
|
| |
| Code: FC-NBR |
|
Insertion Fabric
|
Nylon Anti Wicking Fabric
|
|
Polymer
|
Nitrile (NBR) / Nitrile (NBR)
|
|
Color
|
Black / Black
|
|
Breaking Strength
|
Warp- 225 kgs, Weft- 185 kgs, Warp- 495 lbs, Weft- 407 lbs
|
|
Min. Thickness
|
1.02 mm ± 0.05 mm, 0.04 inch ± 0.002”
|
|
Width Available
|
1.0 Mtr (39.37”) to 1.5 Mtr (60”)
|
|
Coated Fabric Weight
|
1185.5 gsm (± 5%), 34.85 oz/yd2 (± 5%)
|
|
| |
 |
DIAPHRAGM FABRIC
|
Feature
|
|
-
It can be used in Gaskets, Diaphragms and Valve’s Application.
-
It can be easily used at 125˚c temperature.
-
It is good Oil & solvent resistance.
-
It is used for Tank Roofing and Tank Lining.
|
| |
|
|
|
| |
|
Code: FC-NBR
|
|
Insertion Fabric
|
Nylon 66 Fabric
|
|
Polymer
|
Nitrile (NBR) / Nitrile (NBR)
|
|
Color
|
Green / Green
|
|
Breaking Strength
|
Warp- 300 kgs, Weft- 300 kgs, Warp- 660 lbs, Weft- 660 lbs
|
|
Min. Thickness
|
0.75 mm ± 0.05 mm, 0.03 inch ± 0.002”
|
|
Width Available
|
1.0 Mtr (39.37”) to 1.5 Mtr (60”)
|
|
Coated Fabric Weight
|
900 gsm (± 5%), 26.46 oz/yd2 (± 5%)
|
|
| |
 |
| |
BALOONS & PU FLOATS FABRIC
|
Feature
|
|
-
Available in different colors, sizes and thicknesses.
-
Basic product for Floating Seal and defense application.
-
Used in refinery and solvent storage tanks.
-
It follows EIL specification.
-
It is used for manufacturing PU Floats and Balloons.
|
| |
|
|
|
| |
| Code: FC-PU |
|
Insertion Fabric
|
Nylon / polyester
|
|
Polymer
|
Poly urethane (Thermoplastic)
|
|
Color
|
Black / Black
|
|
Breaking Strength
|
Warp- 200 kgs, Weft- 180 kgs, Warp- 440 lbs, Weft- 396 lbs
|
|
Min. Thickness
|
0.4 mm ± 0.05 mm, 0.016 inch ± 0.002”
|
|
Width Available
|
1.0 Mtr (39.37”) to 1.5 Mtr (60”), 500 gsm (± 5%)
|
|
Coated Fabric Weight
|
14.7 oz/yd2 (± 5%)
|
|
| |
 |
|